Features:
1.Rhodium plating layer never change color, has good wear resistance.
2.Gold, platinum, silver and nickel alloy can be directly rhodium plating, plating can be hung and roll plating.
3.Produces bright white rhodium plating.
4. Filling force is very good, fine small trachoma can be filled.
5. Can be plated thick/thin, and will not cause the surface dark.
Model | 100ml (pen or bath electroplating) |
Capacity | 125ml/100mL/4g/5g/2g/0.2g |
Weight | 0.2kg per bottle |
Operating conditions
situation | Unit | range | Ideal range |
Rh | G/L | 1.5-2.5 | 2 |
Tem. | ℃ | 20-60 | 40 |
PH | 0.5-1.5 | 1 | |
|
| 0.2-2.0（rack plating） | 1.0（rack plating） |
Current | A/dm2 | 0.2-0.5（barrel plating） | 0.4（barrel plating） |
Anode efficiency | Mg/Amin | 6 | 3-4 |
Vol. | V | 2.0-3.0 | 2.5 |
Positive/cathode ratio | 1:1-6:1 | 4:1 | |
Agitation | The recommended speed is 5-10cm/ s. Bubbles attached to the plated parts must be removed by beating or shaking to obtain | ||