White Rhodium plating solution 2g 100ml umicore J1
No. :
685
:
:
Features: 1.Rhodium plating layer never change color, has good wear resistance. 2.Gold, platinum, silver and nickel alloy can be directly rhodium plating, plating can be hung and roll plating. 3.Produces bright white rhodium plating. 4. Filling force is very good, fine small trachoma can be filled. 5. Can be plated thick/thin, and will not cause the surface dark.
Model
100ml (pen or bath electroplating)
Capacity
125ml/100mL/4g/5g/2g/0.2g
Weight
0.2kg per bottle
Operating conditions
situation
Unit
range
Ideal range
Rh
G/L
1.5-2.5
2
Tem.
℃
20-60
40
PH
0.5-1.5
1
Current
A/dm2
0.2-2.0（rack plating）
1.0（rack plating）
Current
A/dm2
0.2-0.5（barrel plating）
0.4（barrel plating）
Anode efficiency
Mg/Amin
6
3-4
Vol.
V
2.0-3.0
2.5
Positive/cathode ratio
1:1-6:1
4:1
Agitation
The recommended speed is 5-10cm/ s. Bubbles attached to the plated parts must be removed by beating or shaking to obtain satisfactory results.